ICS27.140 CCSP26 NB 中华人民共和国能源行业标准 NB/T11675-2024 代替DL/T5358-2006 水电工程金属结构设备 防腐蚀技术规程 Technicalcodeforanticorrosionofhydraulicsteel structuresforhydropowerprojects 2024-09-24发布 2025-03-24实施 国家能源局发布NB/T11675-2024 I目次 前言.....................................................................III 引言.......................................................................V 1范围......................................................................1 2规范性引用文件............................................................1 3术语和定义................................................................2 4总体要求..................................................................5 5表面预处理................................................................6 5.1一般要求................................................................6 5.2表面预处理方法及要求....................................................6 5.3涂层修复的表面处理要求..................................................7 5.4质量检验................................................................8 6涂料保护..................................................................8 6.1一般要求................................................................8 6.2涂层系统的选择..........................................................9 6.3涂层配套方案.............................................................9 6.4涂层维护与修复.........................................................10 6.5涂装施工和质量控制.....................................................10 6.6质量检验...............................................................11 7热喷涂金属保护...........................................................11 7.1一般要求...............................................................11 7.2热喷涂金属材料的选择与要求.............................................11 7.3封闭处理及涂装涂料选择.................................................12 7.4热喷涂金属涂层厚度.....................................................12 7.5热喷涂施工和质量控制...................................................13 7.6质量检验...............................................................13 8阴极保护.................................................................14 8.1一般要求...............................................................14 8.2阴极保护准则和电位测量.................................................14NB/T11675-2024 II8.3基本设计资料...........................................................15 8.4牺牲阳极阴极保护.......................................................15 8.5强制电流阴极保护.......................................................16 附录A露点计算.............................................................18 附录B钢材表面清洁度等级...................................................19 附录C热喷涂涂层厚度检测...................................................20 附录D热喷涂涂层结合强度测试方法...........................................21 附录E常用参比电极的主要参数和适用环境.....................................22 附录F无涂层钢常用保护电流密度值和有涂层钢保护电流密度计算.................23 附录G阴极保护设计计算公式.................................................24 附录H常用辅助阳极材料性能.................................................28 图C.1九点十次测量.........................................................21 图D.1切割工具.............................................................22 表1不同涂层系统的表面粗糙度值..............................................7 表2涂层配套方案............................................................9 表3热喷涂金属涂层厚度推荐值...............................................12 表A.1露点计算表...........................................................18 表B.1钢材表面清洁度等级划分表.............................................19 表D.1格子尺寸.............................................................22 表E.1常用参比电极的主要参数和适用环境.....................................22 表F.1无涂层钢常用保护电流密度值...........................................23 表H.1常用辅助阳极材料性能.................................................28NB/T11675-2024 III前言 本文件按照GB/T1.1-2020《标准化工作导则第1部分：标准化文件的结构和起草规则》 的规定起草。 本文件代替DL/T5358-2006《水电水利工程金属结构设备防腐蚀技术规程》，与原规程 相比，除结构调整和编辑性改动外，主要技术变化如下： a）更改了文件适用范围（见第1章，DL/T5358-2006的第1章）； b）增加了“表面粗糙度”“相容性”“维护（涂层）”“封闭处理”的术语和定义（见 第3章）； c）增加了水电工程金属结构设备的腐蚀状况及防腐蚀措施效果巡视检查和定期检测的规 定（见4.0.5）； d）增加了旧涂层维修时进行表面预处理的要求（见5.1.1） e）更改了“质量检验”的一些规定（见5.4，DL/T5358-20