ICS47.020.05 CCSU05 中国船舶工业行业协会团体标准 T/CANSI1—2024 代替T/CANSI1—2018 2024-12-24发布 2025-2-1实施 中国船舶工业行业协会发布船用金属材料试样制备技术要求 Requirementsofspecimenpreparationformarinemetalmaterials 全国团体标准信息平台 全国团体标准信息平台 T/CANSI1—2024 I目次 前言.................................................................................II 1范围................................................................................1 2规范性引用文件......................................................................1 3术语和定义..........................................................................1 4符号................................................................................1 5常用力学性能试样....................................................................2 5.1一般要求........................................................................2 5.2拉伸试样........................................................................3 5.3冲击试样........................................................................6 5.4硬度试样........................................................................8 5.5弯曲试样........................................................................8 5.6管材压扁试样...................................................................10 5.7管材扩口试样...................................................................10 5.8管材卷边试样...................................................................10 5.9断口试样.......................................................................10 6金相试样...........................................................................11 6.1一般要求.......................................................................11 6.2低倍试样.......................................................................11 6.3晶粒度试样.....................................................................12 6.4非金属夹杂物试样...............................................................12 6.5带状组织试样...................................................................13 6.6晶间腐蚀试样（GB/T4334-2020方法E）...........................................13 7化学成分分析试样...................................................................17 7.1一般要求.......................................................................17 7.2屑状试样（用于化学分析方法）的制备.............................................17 7.3块状试样（用于物理分析方法）的制备.............................................19 7.4块状试样（用于氧氮氢分析方法）的制备...........................................19 7.5试样的贮存.....................................................................19 8焊接接头试样.......................................................................19 8.1一般要求.......................................................................19 8.2拉伸试样.......................................................................20 8.3冲击试样.......................................................................21 8.4弯曲试样.......................................................................22 8.5角焊缝折断试样.................................................................24 8.6宏观和硬度试样.................................................................25 附录A（规范性）焊接试件样坯截取......................................................26 全国团体标准信息平台 全国团体标准信息平台 T/CANSI1—2024 II前  言 本文件按照GB/T1.1—2020《标准化工作导则第1部分：标准化文件的结构和起草规则》的规定 起草。 本文件代替T/CANSI1-2018《船用金属材料试样制备技术要求》，与T/CANSI1-2018相比，除结构 调整和编辑性改动外，主要技术变化如下： a)修改了规范性引用文件(见第2章，2018年版的第2章)； b)修改了纵向弧形拉伸试样尺寸（见表5，2018年版的表5）； c)修改了管段拉伸试样的尺寸要求(见5.2.5，2018年版的5.2.5)； d)修改了冲击试样尺寸(见表8，2018年版的表8)； e)修改了弯曲试样尺寸(见5.5.1和5.5.2，2018年版的5.5.1和5.5.2)； f)修改了断口试样尺寸(见表13，2018年版的表13)； g)修改了晶粒度试样的加工要求(见6.3.1，2018年版的6.3.1)； h)修改了晶间腐蚀试样尺寸及制备(见表14，2018年版的表14)； i）增加了块状试样(用于氧氮氢分析方法）的制备(见7.4)； j)修改了熔敷金属试样尺寸(见8.2.2，2018年版的8.2.2)； k)修改了平板弯曲试样尺寸（见表17，2018年版的表18)； 请注意本文件的某些内容可能涉及专利。本文件的发布机构不承担识别专利的责任。 本文件由中国船舶工业行业协会标准化分会提出。 本文件由中国船舶工业行业协会归口。 本文件起草单位：沪东中华造船（集团）有限公司、江南造船（集团）有限责任公司、中国船舶有 限公司第七二五研究所。 本文件起草人：金向红、石东锋、宗晓春、王晓荣、施可扬、周全、周承、沈恩峰、陆旭佳、王大 浩、陆伟、高琛。 本文件于2018年首次发布，本次为第一次修订。 全国团体标准信息平台 全国团体标准信息平台 T/CANSI1—2024 1船用金属材料试样制备技术要求 1范围 本文件规定了船用金属材料常用力学性能试样、金相试样、化学成分分析试样、焊接接头试样制备 的基本要求。 本文件适用于船用金属材料常用理化性能试样的制备。 2规范性引用文件 下列文件中的内容通过文中的规范性引用而构成本文件必不可少的条款。其中